" brass brazing rod /Brass Rods "
The range of Brass Rods manufactured by us is valued for its excellent cutting & drilling performance, high conductivity, and corrosion resistance. These brass tension rods find applications in various sectors mentioned below:
Specifics :-
- Hardware
- Electric & Electronic Components
- Fittings
Forging Brass Rods:-
Our esteemed clients can avail from us a wide gamut of Forging Brass Rods, Extruded Brass Rods which have gained appreciation for it's international quality standards. Available in various sizes, thicknesses and specifications, these brass rods are largely used in various industries. Our competitively priced Forging Brass Rods are acknowledged for their high tensile strength, durable finish standards, corrosion resistance and sturdy designs.
| Chemical Requirements | CuZn42Pb2 | CuZn40Pb2 |
| Copper | 56.5 - 60.0% | 57.0 - 59.0% |
| Lead | 0.60 to 2.0% | 1.5 to 2.5% |
| Iron | 0.30% max | 0.40% max |
| Total Imp. Excl. Iron | 0.20% max | 0.70% max |
| Zinc | Remainder | Remainder |
| Physical Properties | ||
| Tensile Strength | 380 Mpa Min | 40 kg/mm2 Min. |
| Elongation % | 25% Min | 18% Min. |
| Izod Value | - | 2.0 KJ min |
| Fabrication Properties | ||
| Capacity for being | ||
| Cold worked | Poor | Poor |
| Hot formed | Excellent | Excellent |
| Hot forgeability rating | 100% | 100% |
| Machinability Rating | 80% | 80% |
| Suitability for soldering | Excellent | Excellent |
| Suitability for Brazing | Good | Good |
| Uses | ||
| Forged Components, Industrial Valves, Defense components, Watch Case, Automobile Valves Components | ||
High Tensile Brass Rods
We are one of the leading manufacturers, exporters and suppliers of a premium quality assortment of High Tensile Brass Rods, Brass Extrusion Rods. Offered in different sizes, thicknesses and grades, these are valued for their excellent performance, high conductivity, durability, reliable operation and corrosion resistance. At par with the prerequisite industry standards, our High Tensile Brass Rods can be purchased by clients in standard & customized specifications and at cost effective rates.
| Specification : | ||
| High Tensile Brass |
| |
| Total Imp. | 0.50% max | 0.50% max | |||
| Zinc | Remainder | Remainder | |||
| Physical Properties | |||||
| Condition | Size | T.S. MPa | EL% Min | T.S. MPa | EL% Min |
| As manufactured | All Size | 430 min | 20% | 460 min | 20% |
| Cold-worked & Stress | 10-40 | 480 min | 12% | 520 min | 12% |
| Relieved | 40 above | 500 min | 15% | ||
| Uses | |||||
| HT1 is suitable for Soldering | |||||
| Ht2 is suitable for Machining | |||||
Riveting Brass Rods
We are one of the well recognized manufacturers and exporters of a sturdily designed array of Riveting Brass Rods. These are machined in sync with the industrial norms using modern machinery and excellent grade raw materials. Available in diverse specifications and at pocket friendly prices, our Riveting Brass Rods are well known across the global market owing to their incomparable performance, high conductivity, corrosion resistance and low maintenance.
Application Areas:
| Specification : | ||
| Rivetting Brass |
| |
| Physical Properties | |||
| Condition | Size mm | T.S.Kg/mm2 | EL% Min |
| Annealed (O) | 1.2 & above | 28 min. | 30% |
| As Manufactured | 1.2 & above | 35 min. | 25% |
| Uses | |||
| Ductile Alloy Suitable as Blanking, Riveting, Brazing and Upsetting | |||
Application Areas:
- IS: 2074
- BS: 2874 CZ119
- IS: 4170/75
- Cu Zn 38PB1 / 1.5.
Free Cutting Brass Rods
We specialize in manufacturing and exporting our clients a robustly designed range of Free Cutting Brass Rods. These are durable, corrosion resistant and available in different grades, thicknesses and dimensions. Our Free Cutting Brass Rods are manufactured from quality proven raw materials to ensure excellent performance, high conductivity and longer operational life.
Specifications:
Specifications:
- BS249
- IS: 319 Gr. l & ll
- IS: 8364 Gr. l & ll, BS: 2874 CZ121Pb3
- CuZn39Pb3
| Chemical Requirements | Grade I | |
| Copper | 56.0 - 59.0% | |
| Lead | 2.0 to 3.50% | |
| Iron | 0.35% max. | |
| Total Imp. Excl. Iron | 0.70% max. | |
| Zinc | Remainder | |
| Physical Properties | |||
| Condition | Size | T.S. MPA | EL% Min |
| Annealed (O) | 6-25 25-50 50 above | 345 315 285 | 12 17 22 |
| Half-Hard (HB) | 6-12 12-25 25-50 50 above | 405 395 355 325 | 4 6 12 17 |
| Hard (HD) | 6-12 12-25 | 550 490 | - 4 |
| Fabrication Properties | |
| Capacity for being | |
| Cold worked | Poor |
| Cold worked | Poor |
| Hot formed | Fair |
| Machinability Rating | 100% |
| Suitability for soldering | Excellent |
| Suitability for Brazing | Good |
| Uses | |
| Precision Components, Hardware, Hinges, Lock Bodies, Screws, Nuts & Bolts | |
| Physical Properties | |||||
| Condition | Size | T.S. MPA | EL% Min | T.S. MPA | EL% Min |
| Annealed (O) | 6-25 25-50 50 above | 355 305 275 | 15 20 25 | 315 285 255 | 22 27 32 |
| Half-Hard (HB) | 6-12 12-25 25-50 50 above | 395 385 345 | 7 10 15 20 | 355 345 305 285 | 8 12 22 27 |
| Hard (HD) | 6-12 12-25 | 550 485 | 4 | 460 400 | 4 |
| Uses |
| Gr II : Gear, Pinions, Precision, Automobile, Electronic Parts |
| Gr III : Precision Components Machining with Riveting Operation |