Introduction:
This product adopts epoxy resin, functional curing agent, this product has high reactivity, strong adhesive force, high crosslinking density, the coating has excellent chemical resistance, solvent resistance, resistance to cathodic stripping, excellent flexibility, impact resistance and other properties.
Feature:
1. Very good adhesion with the substrate.
2. Good leveling, high gloss coating surface
3. Strong permeability and corrosion resistance
4. The coating has excellent high temperature cathodic disbonding resistance.
5. High surface hardness, strong coating density.
6. Low melting temperature, high reactivity, high curing completion rate.
7. Good mechanical performance, strong flexibility
Power Specification:
|
Test Items |
Technical Indicators |
Test Method |
|
|
Appearance |
Even color, no caking |
||
|
Colour |
As customer required |
visual |
|
|
density(g/cm³) |
1.3-1.5 |
GB/T 4472 |
|
|
Particle size distributor |
150μm Sieve the powder |
≤3.0 |
GB/T 6554-1986 |
|
250μm Sieve the powder |
≤0.2 |
GB/T 6554-1986 |
|
|
non-volatile matter content (%) |
≥ 99.4 |
GB/T 6554-1986 |
|
|
Gel time(s) |
≤ 180s (180℃) ≤ 120s (200℃) ≤ 60s (230℃) |
GB/T 6554-1986 |
|
|
magnetic material content(%) |
≤ 0.002 |
GB/T 2482-1986 |
|
|
Level of liquidity(mm) |
22~28 |
GB/T 6554-1986 |
Coating Specification
|
Test Items |
Technical Indicators |
Test Method |
|||
|
Appearance |
smooth,uniform color, no bubble , no cracking and sinkhole, allow light crack |
visual |
|||
|
Adhesion |
1~3 |
SY/T 0442-1997 |
|||
|
cathodic disbanding resistance 65℃48h(mm) |
≤8 |
SY/T 0413-95 |
|||
|
No cracking |
SY/T 0442-1997 |
||||
|
Electric strength(MV/m) |
≥ 30 |
GB/T 1408-1989 |
|||
|
Impact strength |
≥ 11 |
SY/T 0442-1997 |
|||
|
Resistance to chemical corrosion medium |
10% HCL normal temperature90d 10%H2So4 normal temperature 90d 3.5% Nacl normal temperature 90d 10%NaOH normal temperature 90d |
Qualified
|
GB/T1763-1979 |
||
|
crude 80℃90d gas normal temperature 90d diesel normal temperature 90d kerosene normal temperature 90d |
Qualified
|
GB/T 1733-1993 |
|||
|
abrasive resistance 1000g.1000turn |
≤20g |
GB/T 1768-1979 |
|||
|
Salt spray test(1000h) |
No change |
GB/T1771-1991 |
|||
|
Flatten test (flatten ratio 4/5) |
No cracking |
CJ/T 120-2008 |
|||
Carried Standard:SY/T 0442-97
Application Area: Municipal, water supply, drainage, sewage, circulating water, chemical, thermal and other pipelines.
Applicable process:Electrostatic Coating, inhale coating, dip coating, roller coating
Notes:
1. Steel surface should be no oil and water, surface quality should reach Sa2 1/2 level (GB/T8923), anchor pattern depth 50-90mm, clean dust and abrasive attached to the steel surface, preheat, control temperature in 180-230℃.
2. Product should be stored in ventilated, dry, indoor temperature below 30 ℃, away from heat, corrosive chemicals and chemical solvents, avoid bright light, the maximum stack height should not exceed 4 layers, avoid prolonged pressure, ensure airtight box. In case the clot and damp affects the fluidization performance.
3. To best curing epoxy coating, best anti-corrosion, suggested preheating tube surface temperature in more than 170℃, in order to better improve the curing completion.