Delivery Time:30 working days after received the deposite
Certification:ISO14001:2004, ISO9001:2000
Descrition:
Hentec Industry is dedicated to the development, manufacture and marketing of high-performance aluminum extrusion profiles . We pride ourselves on rapid sampling, flexible production methodologies and world-class technical support to our customers. We have significant experience in the thermal management arena and look forward to working with our customers, wherever they are in the world, and however demanding their needs are. And now, our products have been sold in more than 1000 global customers.
|
Material |
Aluminum alloy |
|
Surface Treatment |
Polishing, Powder coating, Spraying, Anodising, Zinc Plating and etc |
|
Tolerance |
0.02~0.05mm |
|
Equipments |
a) CNC Machining Center b) Extrusion Mchine g)NC Bending Machine h) Anodized /Powder painted line |
|
Preferred Formats |
JPEG, PDF,CAD,IGS,STP |
|
Preferred Industries |
a) Communication Equipments b) Medical Equipments c) House Hardware d) Toy Air soft e) Mechanical Equipments f) Other customized Parts |
Applications:
Aluminum heat sink is widely used on Machines , cars , lighter ...
Specifications:
1. Primary Technical Data
1)Chemical composition
|
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Impurity |
Al |
|
6063 |
0.2-0.6 |
0.35 |
0.1 |
0.1 |
0.45-0.9 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
|
6061 |
0.4-0.8 |
0.7 |
0.15-0.4 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.15 |
Rest |
|
6060 |
0.3-0.6 |
0.1-0.3 |
0.1 |
0.1 |
0.35-0.6 |
- |
0.15 |
0.1 |
0.15 |
Rest |
|
6005 |
0.6-0.9 |
0.35 |
0.1 |
0.1 |
0.40-0.6 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
2) Mechanical property
|
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
|
6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
|
T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
|
|
6061 |
T6 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
Competitive Advantage:
We can offer professional Manufacturing and exporting service, OEM/ODM for Metal & Plastic parts in China. All the parts manufactured by CNC Lathe & Milling Machine Center.