| Properit properties Type | 3YF | 3YP | 3YZ | 3YP-E | 3YZ-E | |
ZrO2(HfO2)% | 94.7 | 94.7 | 94.7 | 94.7 | 94.7 | |
Y2O3% | 5.2+/-0.1 | 5.2+/-0.1 | 5.2+/-0.1 | 5.2+/-0.1 | 5.2+/-0.1 | |
SiO2% ≤ | 0.005 | 0.005 | 0.005 | 0.25 | 0.25 | |
Fe2O3% ≤ | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | |
CaO%≤ | 0.002 | 0.002 | 0.002 | 0.002 | 0.002 | |
MgO≤ | 0.003 | 0.003 | 0.003 | 0.003 | 0.003 | |
TiO2≤ | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
Na2O≤ | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | |
Cl≤ | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
Lgnition%≤ | 0.2 | 0.2 | 2.0 | 0.2 | 2.0 | |
Binder% | 0 | 0 | 1.0 | 0 | 1.0 | |
Sintering Temperature | 1500 | 1500 | 1500 | 1370 | 1370 | |
Sintered Density | 6.05 | 6.05 | 6.05 | 6.05 | 6.05 | |
Three-point Flexural strength(Mpa) | 1000 | 1000 | 1000 | 1000 | 1000 | |
Specific Surface Area(m²/g) | 10+/-1 | 10+/-1 | 10+/-1 | 10+/-1 | 10+/-1 | |
Crystallite Size(nm) | 40-80 | 40-80 | 40-80 | 40-80 | 40-80 | |
Volume Distribution | Dmaxμm | 3 0.5+/-0.1
| 3 0.5+/-0.1 | 3 0.5+/-0.1 | 3 0.5+/-0.1 | 3 0.5+/-0.1 |
Dmin μm | ||||||
Delivery time:
Quantity(Kilograms)1 - 200>200 Est. Time(days)10To be negotiated
Application:
Used in making machinery parts,structural ceramics such as knivers,tools and watch cases,as well as bio ceramics,functional ceramics and other high-tech ceramics.