Advantages of High pressure ceramic plunger:
1. Refractory.
2. Self Lubricating
3. Long Service Life.
4. Good Polished Surface.
5. Environmental and Healthy.
6. Superior Mechanical Strength.
7. High Corrosion and Wear Resistance.
8. Good Insulation Performance Precision.
9. High Temperature and Pressure Resistance.
10. High Purity Zirconia and Alumina Ceramic Material.
Due to these outstanding properties, Ceramic Products are used in a wide range of industrial and advanced appications.
And a lot of practical applications prove that our ceramic products has reached a state of high standard and quality.
Ceramic material composition:
· 95%--99.99% Alumina (Al2O3) · Silicon Carbide · Silicon Nitride
· TTZ: Magnesia partially stabilized Zirconia (ZrO2)
· YTZP: Yttria partially stabilized Zirconia (ZrO2)
· ZDY: Yttria fully stabilized Zirconia (ZrO2)
Properties | Units | AL2O3 | ZrO2 | SiC | Si3N4 |
Density | g/cm3 | 3.65-3.93 | 5.95-6.0 | 3.12 | 3.23 |
Water absorption | 0 | 0 | 0 | 0 | 0 |
Poission`s ratio | / | 0.21-0.22 | 0.3 | 0.17 | 0.26 |
HV hardness hv | MPa | 1650 | 1300-1365 | 2800 | 1500 |
Flexural strength | MPa | 310 | 950 | 390 | 720 |
Heat conductivity | W/m*k | 26-30 | 2-2.2 | 120 | 25 |
Electrical resistivity | Ω*mm2/m | >1016 | >1015 | >103 | >1013 |
Dielectric constant | / | 9.6 | 29 | 9.66-10.03 | / |
Dielectric strength | KV/mm | 8.7 | 9 | / | / |
Coefficientof thermal expansion | 10-16/k | 7.9-8.5 | 10.5 | 3 | 3.2 |
Modulus of elasticity young`s mod | GPa | 280-340 | 210 | 440 | 300 |
Flexural strength(700℃) | MPa | 230 | 210 | 380 | 450 |
Compressive strength | MPa | 2200 | 2000 | 1800 | 2300 |
Max use temperature | ℃ | 1750 | 1050 | 1550 | 1050 |
Resistance to acid alkaline | / | high | high | high | high |
Thermal shock resistance | T(℃) | 180-220 | 280-350 | 230-260 | / |
Fracture toughness | MPa*m1/2 | 4.2 | 10 | 3.9 | 6.2 |
Tensile strength | MPa | 248 | 250 | / | / |