soderberg electrode paste for ferromanganese
low ash, stable quality electrode paste
calcium carbide and ferroalloy use paste
good conductivity
Application and founctions
Electrode paste is used in closed electric smelting furnace as continuous self-baking electrode to produce calcium carbide, and ferroalloy. During the furnace operation, electrode paste acts as current conductor
We can suppy the following types
Specification/Item |
|
|
|
|
|
|
Ash | 4.0%max | 5.0%max | 6.0% Max | 7.0% Max | 9.0% Max | 11.0%Max, |
VM | 12.0%-15.5% | 12.0%-15.5% | 12.0%-15.5% | 9.5%-13.5% | 11.5%-15.5% | 11.5%-15.5% |
Compress Strength | 18.0Mpa Max | 17.0Mpa Max | 15.7Mpa Min | 19.6Mpa Min | 19.6Mpa Min | 19.6Mpa Min |
Specific Resistance | 65μΩm Max | 68μΩm Max | 75μΩm max, | 80μΩm Max | 90μΩm Max | 90μΩm Max |
Bulk Density | 1.38G/CM3 Min | 1.38G/CM3 Min | 1.38G/CM3 Min | 1.38G/CM3 Min | 1.38G/CM3 Min | 1.38G/CM3 Min |