Predominantly Pearlite Cast Steel Mill Liners For AG Mills DF073 With HRC33~42
Negotiable /Ton
Min.Order:1 Ton
Wuxi Orient Anti-wear Engineering Company
Alloy Steel Mill Liners For Ball Mills With More Than HRC50 Hardness DF070
No Leakage Cr-Mo Steel Boltless Mill Lining System With Easier Installation DF083
Ball Mill Liners DF009 Mill Liner Design And Installation With HRC50-55 Hardness
Cement Mill Lining System With HRC50 Hardness And AK50J DF072
Steel Cement Mill Liners For Shipment And Ball Mill With HRC50 DF068
Cast Steel Liners for AG Mills
a. The hardness for Pearlitic CrMo Cast Steel Cap: HRc33~42 (HB310~390);
b. Microstructure: Pearlite;
c. Chemical Composition: Every furnace heat shall be analysed by Spectrometer;
d. Dimensional Checking & Gauging: 100% check as per drawings;
1. By visual inspection;
2. By gauges check;
e. Casting Soundness: Checked by UT test as per international standard.
f. Surface Finish: Visual inspection after shot blasting; To achieve an acceptable level of surface texture, freedom from defects;
g. Reporting: Providing chemical, dimensional and hardness reporats.
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0. |